Abstract Solid residues from agroindustry often accumulate and cause environmental imbalance. An alternative to this is to use this residue as a reinforcement in polymers. The achievement of this work was to characterize a composite with a polystyrene matrix reinforced with Brazil nut shells residues. The residues were cleaned and ground to then produce the samples via injection molding with the proportions of 0%, 2.5% and 5% of load. The specimens were characterized using mechanical tensile testing and thermogravimetric analysis (TGA). The mechanical test showed that the composite with 2.5% of filler had greater stiffness and strength was improved by 5%. Thermal analysis showed an increase in the temperature for the beginning of the degradation of the M2.5 composite. The results confirm a potential application in the automotive industry for the polystyrene composite reinforced with Brazil nut shells.

Abstract The properties of aluminum alloys can be improved by the processing conditions that cause changes in the microstructure and by the addition of alloy elements. In order to understand the physical behavior and mechanical properties of aluminum alloys, it is important to be aware of some of the microstructural characteristics. Some of these characteristics are the morphology, alloy elements, volume and size, and second phase. In this study, we analyzed the effect of annealing on the mechanical and microstructural properties of the laminated AA 5182 aluminum alloy, when subjected to different annealing conditions. The alloy was heated to temperatures of 50º C, 100º C, 150º C, 200º C, 250º C and 300º C for 10 minutes and left to cool naturally. The evolution of the microstructure was characterized by optical and electronic microscopy with EDS, and, to obtain the mechanical properties, a tensile test was performed and the fractures were subsequently analyzed. The results showed that the heat treatment used reduced the amount of second phase particles and this influenced the mechanical properties.

Abstract This study evaluated the influence of cellulose nanocrystals (CNC) content on the properties of epoxy nanocomposites. The CNC were obtained from microcrystalline cellulose by acid hydrolysis. 4.0, 5.5 and 7.0% of untreated CNC were incorporated into epoxy resin. Sonication was used to disperse the CNC in the resin. The thermal stability, the glass transition temperature and the degree of conversion were reduced as observed by Thermogravimetry and Differential Scanning Calorimetry, respectively. The tensile and bending modulus showed no significant improvement and the impact resistance showed a slight reduction due to the non-uniform dispersion of the CNCs, as observed by Transmission Electron Microscopy. Analysis of Scanning Electron Microscopy showed a change of the fracture mechanism of the epoxy resin: the CNCs increased the elastic modulus by reinforcement, but accelerated the fracture by acting as defects. The Halpin-Tsai model was applied to predict the elastic modulus of the epoxy/CNC system.